Application

Cures extremely rapidly to form a glassy, high modulus material Excellent for use in optical applications High refractive index - 1.54 High impact absorption Non-yellowing No oxygen inhibition. Mechanical properties after curing: Modulus*: 930 MPa Strength*: 34 MPa Elongation*: 13% Pencil Hardness: 6H Tack Free**: ﹤2 min*Test Resources: tensile tester, 35 mm gauge length, 1.0 mm thickness, 6.5 mm width.** Cured under stated intensity. Medium pressure mercury bulb with 320-500 nm filter. Adhesion tests were conducted using a cross hatch tape test on films 0.125 mm thick on glass and PET. Material Data using ASTM D 638-02a.

General description

Storage: The storage temperature should not exceed 35 °C. Keep tightly closed. Store in a cool, dry, well-ventilated area. Do not expose to ultraviolet light. High temperatures (>80 °C), pressure, and contamination with peroxides may result in auto-polymerization of the product. Unstable upon depletion of inhibitor.

Packaging

250 g in poly bottle