Application

Cures extremely rapidly to form a glassy high modulus material. Excellent for use in optical applications. High refractive index −1.54. High impact absorption. Non yellowing. No oxygen inhibition. Mechanical properties after curing: Modulus*: 930 MPa Strength*: 34 MPa Elongation*: 13% Pencil hardenss: 6H Tack free**: ﹤2 min *Test Resources: tensile tester, 35 mm gauge length, 1.0 mm thickness, 6.5 mm width.** Cured under stated intensity. Medium pressure mercury bulb with 320-500 nm filter. Adhesion tests were conducted using a cross hatch tape test on films 0.125 mm thick on glass and PET. Material Data using ASTM D 638-02a.

General description

Storage: The storage temperature should not exceed 35°C. Keep tightly closed. Store in a cool, dry, well ventilated area. Do not expose to ultraviolet light. High temperatures (>80°C), pressure and contamination with peroxides may result in auto-polymerization of the product. Unstable upon depletion of inhibitor.