Application

Cures extremely rapidly to form a glassy, high modulus material. Excellent for use in optical applications. High refractive index - 1.54. High impact absorption. Non-yellowing. No oxygen inhibition. Mechanical Properties after curing: Modulus*: 208 MPa Strength*: 7 MPa Elongation*: 54% Pencil Hardness: 6H Tack Free**: 3 min*Test resources: Tensile tester, 35mm gauge length, 1.0 mm thickness, 6.5 mm width.** Cured under stated intensity. Medium pressure mercury bulb with 320-500 nm filter. Adhesion tests were conducted using a cross hatch tape test on films 0.125 mm thick on glass and PET. Material Data using ASTM D 638-02a.

General description

Storage: The storage temperature should not exceed 35 °C. Keep tightly closed. Store in a cool, dry, well-ventilated area. Do not expose to ultraviolet light. High temperatures (>80 °C), pressure and contamination with peroxides may result in auto-polymerization of the product. Unstable upon depletion of inhibitor.